Product Description
Unlocking the Potential of Low Carbon Iron Powder Fe-C: Sinter-Ready for High Strength Components
In the rapidly evolving world of manufacturing and metallurgy, the demand for high-strength components is continually growing. As industries strive for sustainable practices, the use of low carbon iron powder Fe-C sinter-ready materials has emerged as a game-changer.
Low carbon iron powder Fe-C is a specialized material designed for sintering applications. The sintering process involves compacting and forming a solid mass of material using heat, without melting it to the point of liquefaction. This method is integral in manufacturing high-strength components, especially in the automotive and aerospace sectors.
- High Purity: Low carbon iron powder Fe-C is characterized by its high purity, ensuring minimal impurities that can affect the strength and durability of the final product.
- Controlled Particle Size: The powder is engineered to have a consistent particle size, which is crucial for uniform sintering and achieving desired mechanical properties.
- Low Carbon Content: As the name suggests, this powder has a reduced carbon content, which is pivotal in minimizing carbide formation that can compromise the toughness of the components.
| Property | Iron-Based Alloy Powders | Stainless Steel (316L) | Nickel Alloys (Inconel 625) | Titanium (Ti-6Al-4V) |
| Density (g/cm³) | 7.4–7.9 (varies by alloy) | 7.9 | 8.4 | 4.4 |
| Hardness (HRC) | 20–65 (depends on heat treatment) | 25–35 | 20–40 (annealed) | 36–40 |
| Tensile Strength (MPa) | 300–1,500+ | 500–700 | 900–1,200 | 900–1,100 |
| Corrosion Resistance | Moderate (improves with Cr/Ni) | Excellent | Excellent | Excellent |
| Max Operating Temp. (°C) | 500–1,200 (alloy-dependent) | 800 | 1,000+ | 600 |
| Cost (vs. Pure Fe = 1x) | 1x–5x (alloy-dependent) | 3x–5x | 10x–20x | 20x–30x |
Injection molding of powder injection molding technology
Compared with traditional process, with high precision, homogeneity, good performance, low production cost, etc. In recent years, with the rapid development of MIM technology, its products have been widely used in consumer electronics, communications and information engineering, biological medical equipment, automobiles, watch industry, weapons and aerospace and other industrial fields.
| Grade | Chemical Nominal Composition(wt%) |
| Alloy | C | Si | Cr | Ni | Mn | Mo | Cu | W | V | Fe |
| 316L | | | 16.0-18.0 | 10.0-14.0 | | 2.0-3.0 | - | - | - | Bal. |
| 304L | | | 18.0-20.0 | 8.0-12.0 | | - | - | - | - | Bal. |
| 310S | | | 24.0-26.0 | 19.0-22.0 | | - | - | - | - | Bal. |
| 17-4PH | | | 15.0-17.5 | 3.0~5.0 | | - | 3.00-5.00 | - | - | Bal. |
| 15-5PH | | | 14.0-15.5 | 3.5~5.5 | | - | 2.5~4.5 | - | - | Bal. |
| 4340 | 0.38-0.43 | 0.15-0.35 | 0.7-0.9 | 1.65-2.00 | 0.6-0.8 | 0.2-0.3 | - | - | - | Bal. |
| S136 | 0.20-0.45 | 0.8-1.0 | 12.0-14.0 | - | | - | - | - | 0.15-0.40 | Bal. |
| D2 | 1.40-1.60 | | 11.0-13.0 | - | | 0.8-1.2 | - | - | 0.2-0.5 | Bal. |
| H11 | 0.32-0.45 | 0.6-1 | 4.7-5.2 | - | 0.2-0.5 | 0.8-1.2 | - | - | 0.2-0.6 | Bal. |
| H13 | 0.32-0.45 | 0.8-1.2 | 4.75-5.5 | - | 0.2-0.5 | 1.1-1.5 | - | - | 0.8-1.2 | Bal. |
| M2 | 0.78-0.88 | 0.2-0.45 | 3.75-4.5 | - | 0.15-0.4 | 4.5-5.5 | - | 5.5-6.75 | 1.75-2.2 | Bal. |
| M4 | 1.25-1.40 | 0.2-0.45 | 3.75-4.5 | - | 0.15-0.4 | 4.5-5.5 | - | 5.25-6.5 | 3.75-4.5 | Bal. |
| T15 | 1.4-1.6 | 0.15-0.4 | 3.75-5.0 | - | 0.15-0.4 | - | - | 11.75-13 | 4.5-5.25 | Bal. |
| 30CrMnSiA | 0.28-0.34 | 0.9-1.2 | 0.8-1.1 | - | 0.8-1.1 | - | - | - | - | Bal. |
| SAE-1524 | 0.18-0.25 | - | - | - | 1.30-1.65 | - | - | - | - | Bal. |
| 4605 | 0.4-0.6 | | - | 1.5-2.5 | - | 0.2-0.5 | - | - | - | Bal. |
| 8620 | 0.18-0.23 | 0.15-0.35 | 0.4-0.6 | 0.4-0.7 | 0.7-0.9 | 0.15-0.25 | - | - | - | Bal. |
Powder specification:
| Particle Size | Tapping Density | Particle Size Distribution(μm) |
| | (g/cm³) | D10 | D50 | D90 |
| D50:12um | ＞4.8 | 3.6- 5.0 | 11.5-13.5 | 22-26 |
| D50:11um | ＞4.8 | 3.0- 4.5 | 10.5-11.5 | 19-23 |
Factory equipment
Exhibition & Partner
Case
Ship to Poland
Ship to Germany
FAQ
1. What types of stainless steel powders are used in 3D printing?
-
Common grades include 316L (excellent corrosion resistance), 17-4 PH (high strength and hardness), 304L (general-purpose use), and 420 (wear resistance). Each grade has specific properties suited for different applications.
2. What is the typical particle size for stainless steel powders in 3D printing?
3. Can stainless steel powders be reused?
-
Yes, unused powder can often be recycled by sieving and blending with fresh powder. However, excessive reuse can degrade powder quality, so regular testing is recommended.
4. What safety precautions should be taken when handling stainless steel powders?
-
Avoid inhalation or skin contact by using gloves, masks, and protective clothing.
-
Store powders in a dry, airtight container to prevent moisture absorption.
-
Handle powders in a well-ventilated area or under inert gas to minimize explosion risks.